Fabrication

Mo-Si-B alloys are a leading candidate for the next generation of jet turbine engine blades and have the potential to raise the operating temperatures by 300-400C, which would dramatically increase power and efficiency. The alloys of interest are a three-phase mixture of the molybdenum solid solution (Moss) and two intermetallic phases, Mo3Si (A15) and Mo5SiB2 (T2). A novel powder metallurgical method was developed which uses the reaction of molybdenum, silicon nitride (Si3N4) and boron nitride (BN) powders to synthesize a fine dispersion of the intermetallic phases in a Moss matrix. The covalent nitrides are stable in oxidizing environments up to 1000C, allowing for fine particle processing without the formation of silicon and boron oxides. The process developed uses standard powder processing techniques to create Mo-Si-B alloys in a less complex and expensive manner than previously demonstrated. The formation of the intermetallic phases was examined by thermo-gravimetric analysis and x-ray diffraction. The start of the reactions to form the T2 and A15 phases were observed at 1140C and 1193C and the reactions have been demonstrated to be complete in as little as two hours at 1300C. This powder metallurgy approach yields a fine dispersion of intermetallics in the Moss matrix, with average grain sizes of 2-4mum. Densities up to 95% of theoretical were attained from pressureless sintering at 1600C and full theoretical density was achieved by hot-isostatic pressing (HIP). Low temperature sintering and HIPing was attempted to limit grain growth and to reduce the equilibrium silicon concentration in the Moss matrix. Sintering and HIPing at 1300C reduced the grain sizes of all three phases by over a factor of two. Powder metallurgy provides an opportunity for microstructure control through changes in raw materials and processing parameters. Microstructure examination by electron back-scatter diffraction (EBSD) imaging was used to precisely define the location of all three phases and to measure the volume fractions and grain size distributions. Microstructural quantification techniques including two-point correlation functions were used to quantify microstructural features and correlate the BN powder size and morphology to the distribution of the intermetallic phases. High-temperature tensile tests were conducted and yield strengths of 580MPa at 1100C and 480MPa at 1200C were measured for the Mo-2Si-1B wt.% alloy. The yield strength of the Mo-3Si-1B wt.% alloy was 680MPa at 1100C and 420MPa at 1300C. A review of the pertinent literature reveals that these are among the highest yield strengths measured for these compositions. The oxidation resistance in air at 1000 and 1100C was found to be comparable to the best values reported in the literature. The protective borosilicate surface layer was formed quickly due to the close spacing of intermetallic particles and pre-oxidation treatment was developed to further limit the transient oxidation behavior. An oxidation model was developed which factors in the different stages of oxidation to predict compositions which minimize the total metal recession due to oxidation.